Study on tensile fracture failure of a steel plate with a surface crack
,
 
,
 
,
 
,
 
Tao Li 1
 
 
 
More details
Hide details
1
School of Mechanical and Electrical Engineering, Hubei Polytechnic University, Huangshi, China
 
2
PipeChina Southwest Pipeline Co., Ltd, Jinniu District, Chengdu, China
 
 
Submission date: 2022-05-01
 
 
Final revision date: 2023-01-18
 
 
Acceptance date: 2023-04-03
 
 
Online publication date: 2023-04-24
 
 
Publication date: 2023-04-28
 
 
Corresponding author
Zhewen Chong   

School of Mechanical and Electrical Engineering, Hubei Polytechnic University, China
 
 
Journal of Theoretical and Applied Mechanics 2023;61(2):343-354
 
KEYWORDS
TOPICS
ABSTRACT
In order to study the effect of different surface crack parameters on the fracture failure of steel plate, the model was established by FEM. The results showed that the edge surface crack has the greatest influence on the fracture failure of the steel plate, and for non-edge surface cracks, the central surface crack has the greatest influence on the fracture failure of the steel plate. The larger the a/t and the smaller the a/c, the easier the steel plate fracture failure occurs. The a/c has a certain influence on the variation law of K and the position where Kmax appears.
 
REFERENCES (25)
1.
Anderson T.L., 2017, Fracture Mechanics: Fundamentals and Applications, CRC Press.
 
2.
Barsoum R.S., 1975, Further application of quadratic isoparametric finite elements to linear fracture mechanics of plate bending and general shells, International Journal of Fracture, 11, 1, 167-169.
 
3.
Chandra S.K., Sarkar R., Bhowmick A.D., De P.S., Chakraborti P.C., Ray S.K., 2020, Evaluation of ductile tearing resistance of an interstitial free steel sheet using SENT specimens, Engineering Fracture Mechanics, 238, 107257.
 
4.
Cheng Z., Wang H., Liu G.-R., 2021, Fatigue crack propagation in carbon steel using RVE based model, Engineering Fracture Mechanics, 258.
 
5.
Chong Z., Ma T., Yu D., Wu D., Tao J., Lv H., 2021, Stress intensity factor of double cracks on seabed-spanning pipeline surface under the spring boundary, Journal of Pipeline Systems Engineering and Practice, 12, 4.
 
6.
Di Gioacchino F., Lucon E., Mitchell E.B., Clarke K.D., Matlock D.K., 2021, Side-grooved Charpy impact testing: Assessment of splitting and fracture properties of high-toughness plate steels, Engineering Fracture Mechanics, 252, 107842.
 
7.
Dolbow J., Moës N., Belytschko T., 2000, Modeling fracture in Mindlin-Reissner plates with the extended finite element method, International Journal of Solids and Structures, 37, 48-50, 7161-7183.
 
8.
Figiel Ł., Kamiński M., 2009, Numerical probabilistic approach to sensitivity analysis in a fatigue delamination problem of a two-layer composite, Applied Mathematics and Computation, 209, 1, 75-90.
 
9.
He Y., Li L., Lu Z., et al., 2020, Analysis on abnormal tensile fracture of a certain high strength steel (in Chinese), Materials Protection, 53, 2, 157-161.
 
10.
Henshell R.D., Shaw K.G., 1975, Crack tip finite elements are unnecessary, International Journal for Numerical Methods in Engineering, 9, 3, 495-507.
 
11.
Lee Y.-S., Kim S., Jang D.-W., Lee S.-B., 2022, Mechanism of crack initiation and propagation in high-alloy steel slabs during the cooling and scarfing processes after the continuous casting process, Mechanics of Materials, 166, 104240.
 
12.
Li Z., Jiang X., Hopman H., Zhu L., Liu Z., 2020, Numerical investigation on the surface crack growth in FRP-reinforced steel plates subjected to tension, Theoretical and Applied Fracture Mechanics, 108.
 
13.
Lin X.B, Smith R.A., 1999, Finite element modelling of fatigue crack growth of surface cracked plates. Part I: The numerical technique, Engineering Fracture Mechanics, 63, 5, 503-522.
 
14.
Liu J., Xin H., Zhao X.-L., 2023, Prediction of fatigue crack propagation in center cracked steel plate strengthened with prestressed CFRP strip, Thin-Walled Structures, 183, 110416.
 
15.
Newman Jr. J.C., Raju I.S., 1984, Stress-Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies Subjected to Tension and Bending Loads, National Aeronautics and Space Administration (NASA), Langley Research Center, Hampton, VA.
 
16.
Omiya M., Arakawa S., Yao Z., Muramatsu M., Nishi S., Takada K., Murata M., Okato K., Ogawa K., Oide K., Kobayashi T., Han J., Terada K., 2022, Influence of strength and notch shape on crack initiation and propagation behavior of advanced high strength steel sheets, Engineering Fracture Mechanics, 271, 108573.
 
17.
Rice J.R., 1968, A path independent integral and the approximate analysis of strain concentration by notches and cracks, Journal of Applied Mechanics, 35, 2, 379-386.
 
18.
Saber A., Shariati M.R., Nejad M., 2020, Experimental and numerical investigation of effect of size, position and geometry of some cutouts on fatigue life and crack growth path on AISI1045 steel plate, Theoretical and Applied Fracture Mechanics, 107, 102506.
 
19.
Shahani A.R., Shodja M.M., Shahhosseini A., 2010, Experimental investigation and finite element analysis of fatigue crack growth in pipes containing a circumferential semi-elliptical crack subjected to bending, Experimental Mechanics, 50, 5, 563-573.
 
20.
Wen Y., 2020, Research on Fracture Performance of Corroded Steel Plate with Central Crack, Xi’an: Xi’an University of Architecture and Technology.
 
21.
Yuan P., Fu D., Gao Y., et al., 2021, Causes analysis and improvement measures for surface cracks of Q235B steel plate (in Chinese), Wide ang Heavy Plate, 27, 6, 34-36.
 
22.
Zhang H., Xu S., Nie B., Wen Y., 2019, Effect of corrosion on the fracture properties of steel plates, Construction and Building Materials, 225, 20, 1202-1213.
 
23.
Zhang K., Wang M., Liu W., Liu J., 2021, Fracture prediction for an advanced high-strength steel sheet using the fully coupled elastoplastic damage model with stress-state dependence, Acta Mechanica Solida Sinica, 34, 263-273.
 
24.
Zhang Q., 2020, Study on Mechanical Response of Q235 Steel and Constitutive Model under Cyclic Loading, Hebei: Yanshan University.
 
25.
Zhang S.Q., Jiao S.H., Ding J.H., Zhang Q.F., Jiang H.S., 2018, Simulation study on shear crack of steel plate, Materials Science Forum, 941, 480-485.
 
eISSN:2543-6309
ISSN:1429-2955
Journals System - logo
Scroll to top